The effect of thickness on surface structure of rf sputtered TiO2 thin films by XPS, SEM/EDS, AFM and SAM
Author
Sirkeci, Merve
Özçelik, Süleyman
Bingöl, Doğukan
Kınacı, Barış
Ünlü, M. Burçin
Güzelçimen, Feyza
Tanören, Bükem
Çetinkaya, Çağlar
Kaya, Meltem Dönmez
Efkere, H. İbrahim
Özen, Yunus
Metadata
Show full item recordAbstract
In the current study, silicon was utilized as the substrate material and, then, the TiO2depositions with 100nm, 300nm, 500nm and 700nm were done onto substrates as thin films at room temperature by a radio frequency (rf) magnetron sputtering method. The binding energy, the surface roughness, elemental analysis and the specific acoustic impedance have been determined via X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), scanning electron microscopy/energy dispersive spectroscopy (SEM/EDS) and scanning acoustic microscopy (SAM), respectively. AFM analysis represented that the root mean square roughness values changed in the range of 0.72nm–1.22nm, gradually by the increase in thickness. Two-dimensional acoustic images were recorded by SAM with 80MHz transducer. The mean and standard deviation values of acoustic impedance were found as 3.151±0.080 MRayl for 100nm, 3.366±0.080 MRayl for 300nm, 3.379±0.067 MRayl for 500nm and, 3.394±0.065 MRayl for 700nm. SAM results pointed out that the hardness of films increased with increasing thickness. Moreover, the surface defects at the micrometer level were demonstrated. The success of imaging films indicated the potential of SAM in monitoring as well as the inspection of flat two-dimensional surfaces.
Collections
- Makale [92796]